Segregation in concrete

Segregation in concrete is a case of particle segregation in concrete applications, in which particulate solids tend to segregate by virtue of differences in the size, density, shape and other properties of particles of which they are composed. when the workability of concrete is high under pouring conditions, or the amount of mortar is larger than the void volume of coarse aggregate, or the particle size of aggregate is not ideal, excessive vibration can cause segregation bleeding or lighter weight^[1]

YouTube Encyclopedic

1/3
Views:
17 066
3 705
2 065

Transcription

Definition

It is described by American Society for Testing and Materials as follows: "Segregation in concrete is commonly thought of as separation of some size groups of aggregates from cement mortar^[nb 1] in isolated locations with corresponding deficiencies of these materials in other locations. Segregation results in proportions of the laid concrete being in variation with those designed.^[3]^: 38 Segregation could result from internal factors such as concrete that is not proportioned properly and not mixed adequately, or too workable a mix. It also could result from external factors such as too much vibration,^[nb 2] improper transportation, placement, or adverse weather conditions.^[4]^: 7, 8 The corresponding increase in proportion of cement paste in upper areas would tend to make them susceptible to increased shrinkage and formation of cracks. These cracks could be 10 μm to 500 μm wide, formed perpendicular to the surface, and be in the form of map patterns."^[5]^: 149

The concrete should be free from segregation. It is defined as the breaking up of cohesion (separation of concrete aggregate) in a mass of concrete. It results in honey-combing, decrease in density, and ultimately loss of strength of hardened concrete. The effect of aggregate segregation on the mechanical and transport behavior of concrete has been the focus of both modeling as well as experimental investigation.

Notes

^ Mortar is a mixture of fine aggregates and cement, that in concrete acts as a binder between particles of coarse aggregates.^[2]^{: 119, 120}
^ Compaction describes the process employed to obtain maximum density in concrete after it has been deposited in place. Compaction could be achieved by mechanical vibrators, devices that vibrate at various frequencies and which transfer these vibrations to concrete.^[2]^: 144

References

^ execution, construction (10 October 2021). "what happens if over vibration of concrete". Civil Experience. Archived from the original on August 23, 2021. Retrieved August 23, 2021.
^ ^a ^b Ttti Chandigarh (1 July 2001). Civil Engineering Materials. Tata McGraw-Hill Education. ISBN 978-0-07-460431-1. Retrieved 20 May 2012.
^ American Society for Testing Materials. Committee C-9 on Concrete and Concrete Aggregates (1 January 1956). Significance of Tests and Properties of Concrete and Concrete Aggregates: A Résumé of Present Information on the Significance of the Properties of Concrete and Concrete Aggregates and the Tests by which They are Studied and Determined. ASTM International. GGKEY:SL4DFHZUPJ6. Retrieved 20 May 2012.{{cite book}}: CS1 maint: numeric names: authors list (link)
^ Sybil K. Reinert; Iowa State University. Civil, Construction, and Environmental Engineering (2007). Optimizing Portland Cement Concrete Mix Design to Environmental and Construction Variables with the Aid of Computer Design Software. ISBN 978-0-549-33432-3. Retrieved 20 May 2012.{{cite book}}: CS1 maint: multiple names: authors list (link)
^ Ravindra K. Dhir; Mukesh C. Limbachiya (1999). Utilizing Ready Mix Concrete and Mortar: Proceedings of the International Conference Held at the University of Dundee, Scotland, UK on 8-10 September 1999. Thomas Telford. ISBN 978-0-7277-2823-4. Retrieved 20 May 2012.

External links

Segregation in concrete - from Civil Experiences
Lecture 12: Module 5 Lecture - 4 Fresh Concrete : Segregation & Bleeding – from the Indian Institute of Technology, Delhi

v t e Concrete
History	Ancient Roman architecture Roman architectural revolution Roman concrete Roman engineering Roman technology
Composition	Cement Calcium aluminate Energetically modified Portland Rosendale Water Water–cement ratio Aggregate Reinforcement Fly ash Ground granulated blast-furnace slag Silica fume Metakaolin
Production	Plant Concrete mixer Volumetric mixer Reversing drum mixer Slump test Flow table test Curing Concrete cover Cover meter Rebar
Construction	Precast Cast-in-place Formwork Climbing formwork Slip forming Screed Power screed Finisher Grinder Power trowel Pump Float Sealer Tremie
Science	Properties Durability Degradation Environmental impact Recycling Segregation Alkali–silica reaction
Types	AstroCrete Fiber-reinforced Filigree Foam Lunarcrete Mass Nanoconcrete Pervious Polished Polymer Prestressed Ready-mix Reinforced Roller-compacting Self-consolidating Self-leveling Sulfur Tabby Translucent Aerated AAC RAAC
Applications	Slab waffle hollow-core voided biaxial slab on grade Concrete block Step barrier Roads Columns Structures
Organizations	American Concrete Institute Concrete Society Institution of Structural Engineers Indian Concrete Institute Nanocem Portland Cement Association International Federation for Structural Concrete
Standards	Eurocode 2 EN 197-1 EN 206-1 EN 10080
See also	Hempcrete
Category:Concrete

This article about a civil engineering topic is a stub. You can help Wikipedia by expanding it.

This page was last edited on 29 May 2024, at 12:14

From Wikipedia, the free encyclopedia