To install click the Add extension button. That's it.

The source code for the WIKI 2 extension is being checked by specialists of the Mozilla Foundation, Google, and Apple. You could also do it yourself at any point in time.

4,5
Kelly Slayton
Congratulations on this excellent venture… what a great idea!
Alexander Grigorievskiy
I use WIKI 2 every day and almost forgot how the original Wikipedia looks like.
Live Statistics
English Articles
Improved in 24 Hours
Added in 24 Hours
What we do. Every page goes through several hundred of perfecting techniques; in live mode. Quite the same Wikipedia. Just better.
.
Leo
Newton
Brights
Milds

From Wikipedia, the free encyclopedia

Flash welding is a type of resistance welding that does not use any filler metals. The pieces of metal to be welded are set apart at a predetermined distance based on material thickness, material composition, and desired properties of the finished weld. Current is applied to the metal, and the gap between the two pieces creates resistance and produces the arc required to melt the metal. Once the pieces of metal reach the proper temperature, they are pressed together, effectively forge welding them together.[1]

Parameters

According to a study published in Materials and Design, several parameters affect the final product. Flash time is the time that the arc is present. Upset time is the amount of time that the two pieces are pressed together. Flash time needs to be long enough to sufficiently heat the metal before it is pressed together. However, if it is too long, too much of the base metal begins to melt away. The upset time is critical in creating the desired mechanical properties of the finished weld. During the upset, any impurities in the base metal are pressed out creating a perfect weld. If the upset time is too short, some of the impurities may remain in the base metal creating a defective weld. The upset time is also crucial in the strength of the finished weld because it is during the upset that coalescence occurs between the two pieces of metal. If the upset time is too short, the two pieces of metal may not completely bond.[1]

Very often flash butt welding is controlled by distance rather than time such that the flashing would occur for a pre-determined length, say 5 mm, before the upsetting cycle starts. Upsetting may then also be controlled by distance. A parameter would be set to apply the upsetting force until a certain distance has been upset. It is generally the upsetting distance that is more important than the upsetting time.

At the end of upsetting there is commonly a 'hold time' during which the joint is held still to allow the joint to cool and the two pieces of metal to completely bond.

Applications

According to the Journal of Materials Processing, the railroad industry uses flash welding to join sections of mainline rail together to create continuous welded rail (CWR), which is much smoother than mechanically-joined rail because there are no gaps between the sections of rail. This smoother rail reduces the wear on the rails themselves, effectively reducing the frequency of inspections and maintenance.[2] Continuous welded rail is particularly used on high-speed rail lines because of the smoothness of the rail head. A study published in Materials Science and Design proved that flash welding is also beneficial in the railroad industry because it allows dissimilar metals, including non ferrous metals, to be joined. This allows switches and crossings, which are generally composed of high manganese steel, to be effectively welded to carbon steel rail with the use of a stainless steel insert, while keeping the desired mechanical properties of both the rails and the crossings intact.[3] The ability of this single process to weld many different metals, with simple parameter adjustments, makes it very versatile. Materials and Design also discusses the use of flash welding in the metal building industry to increase the length of the angle iron used to fabricate joists.[1]

The aluminum industry uses flash welding to join aluminum, steel, and copper in various current-carrying conductors called busbars. The steel is used for strength, the copper is used for conductivity, and the aluminum is used for its combination of cost and conductivity.[4]

See also

References

  1. ^ a b c Ziemian, Constance W.; Sharma, Mala M.; Whaley, Donald E. (2012). "Materials and Design". Materials & Design. 33: 175–184. doi:10.1016/j.matdes.2011.07.026.
  2. ^ Tawfik, David; Mutton, Peter John; Chiu, Wing Kong (2008). "Journal of Materials Processing Technology". Journal of Materials Processing Technology. 196 (1–3): 279–291. doi:10.1016/j.jmatprotec.2007.05.055.
  3. ^ Zhang, Fucheng; Lv, Bo; Hu, Baitao; Li, Yanguo (2007). "Materials Science and Engineering". Materials Science and Engineering: A. 454-455: 288–292. doi:10.1016/j.msea.2006.11.018.
  4. ^ http://www.jbmincorporated.com/product-gallery/flash-welding/
This page was last edited on 10 November 2019, at 09:51
Basis of this page is in Wikipedia. Text is available under the CC BY-SA 3.0 Unported License. Non-text media are available under their specified licenses. Wikipedia® is a registered trademark of the Wikimedia Foundation, Inc. WIKI 2 is an independent company and has no affiliation with Wikimedia Foundation.