Coke Strength after Reaction (CSR) refers to coke "hot" strength, generally a quality reference in a simulated reaction condition in an industrial blast furnace. The test is based on a procedure developed by Nippon Steel Corp in the 1970s as an attempt to get an indication of coke performance and is used widely throughout the world since then. It is one of the major considerations when blending coking coal for export sale.[1]
YouTube Encyclopedic
-
1/3Views:9 420 3721 228 529219 379
-
Shocking Before-And-After Drug Use Photos
-
Gallium Induced Structural Failure of an Aluminum Sheet
-
Gallium Induced Structural Failure of an Aluminum Baseball Bat
Transcription
Test procedure
In the test, a 200 g sample of 19–21 mm particle range coke is heated at 1100°C under 1 atmosphere pressure of carbon dioxide for 2 hours. The coke is preheated and cooled under nitrogen and the weight loss during reaction is measured. The percentage weight loss is known as the reactivity (CRI). The reacted coke is placed in an I-type drum (no lifters) and subjected to 600 revolutions in 30 minutes. The percent of carbon material removed from the drum that is ≥10 mm is known as the coke strength after reaction (CSR). [2]
References
- ^ "Metallurgical Coke or Blast Furnace Coke for iron and steel industry". Archived from the original on 2011-07-08. Retrieved 2011-02-11.
- ^ Reifensteinin (2003) ACARP Report C12004 Coke Reactivity Test: Critical Parameters
 | This material-related article is a stub. You can help Wikipedia by expanding it. |
This page was last edited on 7 April 2023, at 14:48