41xx steel is a family of SAE steel grades, as specified by the Society of Automotive Engineers (SAE). Alloying elements include chromium and molybdenum, and as a result these materials are often informally referred to as chromoly steel (common variant stylings include chrome-moly, cro-moly, CrMo, CRMO, CR-MOLY, and similar). They have an excellent strength to weight ratio and are considerably stronger and harder than standard 1020 steel, but are not easily welded, requiring thermal treatment both before and after welding to avoid cold cracking.[1]
While these grades of steel do contain chromium, it is not in great enough quantities to provide the corrosion resistance found in stainless steel.
Examples of applications for 4130, 4140, and 4145 include structural tubing, bicycle frames, gas bottles for transportation of pressurized gases, firearm parts, clutch and flywheel components, and roll cages. 4150 stands out as being one of the steels accepted for use in M16 rifle and M4 carbine barrels by the United States military. These steels are also used in aircraft parts and therefore 41xx grade structural tubing is sometimes referred to as "aircraft tubing".
YouTube Encyclopedic
-
1/3Views:105 75564 8386 280
-
How Buildings Are Engineered To NOT Collapse - What Structural Engineers Actually Do
-
5 Free Licensed Structural Engineering Software with No Expiration | Free Software Downloads
-
Top 6 Structural Engineers in the World
Transcription
Properties
| SAE grade | Cr | Mo | C[a] | Mn | P, max. | S, max. | Si |
|---|---|---|---|---|---|---|---|
| 4118 | 0.40–0.60 | 0.08–0.15 | 0.18–0.23 | 0.70–0.90 | 0.035 | 0.040 | 0.15–0.35 |
| 4120 | 0.40–0.60 | 0.13–0.20 | 0.18–0.23 | 0.90–1.20 | 0.035 | 0.040 | 0.15–0.35 |
| 4121 | 0.45–0.65 | 0.20–0.30 | 0.18–0.23 | 0.75–1.00 | 0.035 | 0.040 | 0.15–0.35 |
| 4130 | 0.80–1.10 | 0.15–0.25 | 0.28–0.33 | 0.40–0.60 | 0.035 | 0.040 | 0.15–0.35 |
| 4135 | 0.80–1.10 | 0.15–0.25 | 0.33–0.38 | 0.70–0.90 | 0.035 | 0.040 | 0.15–0.35 |
| 4137 | 0.80–1.10 | 0.15–0.25 | 0.35–0.40 | 0.70–0.90 | 0.035 | 0.040 | 0.15–0.35 |
| 4140 | 0.80–1.10 | 0.15–0.25 | 0.38–0.43 | 0.75–1.00 | 0.035 | 0.040 | 0.15–0.35 |
| 4142 | 0.80–1.10 | 0.15–0.25 | 0.40–0.45 | 0.75–1.00 | 0.035 | 0.040 | 0.15–0.35 |
| 4145 | 0.80–1.10 | 0.15–0.25 | 0.43–0.48 | 0.75–1.00 | 0.035 | 0.040 | 0.15–0.35 |
| 4147 | 0.80–1.10 | 0.15–0.25 | 0.45–0.50 | 0.75–1.00 | 0.035 | 0.040 | 0.15–0.35 |
| 4150 | 0.80–1.10 | 0.15–0.25 | 0.48–0.53 | 0.75–1.00 | 0.035 | 0.040 | 0.15–0.35 |
| 4161 | 0.70–0.90 | 0.25–0.35 | 0.56–0.64 | 0.75–1.00 | 0.035 | 0.040 | 0.15–0.35 |
| |||||||
| Material | Condition | Tensile strength | Yield strength | Elongation at fracture, 2-inch gauge [%] |
Hardness, Rockwell |
|---|---|---|---|---|---|
| 4130 | Cold drawn, normalized[3] | 85–110 ksi (590–760 MPa) | 70–85 ksi (480–590 MPa) | 20–30 | B 90–96 |
| 4142 | Hot rolled, annealed[3] | 90–100 ksi (620–690 MPa) | 60–70 ksi (410–480 MPa) | 20–30 | B 90–95 |
| Cold drawn, annealed[3] | 105–120 ksi (720–830 MPa) | 85–95 ksi (590–660 MPa) | 15–25 | B 96–100 | |
| 4150 | Hot rolled, annealed[3] | 90–110 ksi (620–760 MPa) | 65–75 ksi (450–520 MPa) | 20–30 | B 90–96 |
Other characteristics
One of the characteristics of this class of steel is the ability to be case hardened by carburization of the surface. The core of the material retains its bulk properties, while the outer surface is significantly hardened to reduce wear and tear. This makes this grade of steel an excellent material for uses such as gears, piston pins, and crankshafts.[2]
4140 Steel
4140 Steel[4] (Quenched and Tempered) Mechanical Properties
| Diameter | d ≤ 16 | 16 < d ≤ 40 | 40 < d ≤ 100 | 100 < d ≤ 160 | 160 < d ≤ 250 |
|---|---|---|---|---|---|
| Thickness | t ≤ 8 | 8 < t ≤ 20 | 20 < t ≤ 60 | 60 < t ≤ 100 | 100 < t ≤ 160 |
| Tensile Strength | 160–190 ksi (1,100–1,300 MPa) | 150–170 ksi (1,000–1,200 MPa) | 130–160 ksi (900–1,100 MPa) | 116–138 ksi (800–950 MPa) | 109–131 ksi (750–900 MPa) |
| Yield Strength (Min) | 130 ksi (900 MPa) | 109 ksi (750 MPa) | 94 ksi (650 MPa) | 80 ksi (550 MPa) | 73 ksi (500 MPa) |
| Elongation (% Min) | 10 | 11 | 12 | 13 | 14 |
| Reduction (% Min) | 40 | 45 | 50 | 50 | 55 |
| Impact Strength (J) ≥ | - | 26 ft⋅lbf (35 J) | 26 ft⋅lbf (35 J) | 26 ft⋅lbf (35 J) | 26 ft⋅lbf (35 J) |
See also
- 4116 Krupp, not a member of this series
References
- ^ Metals, Online. "Online Metal Store | Small Quantity Metal Orders | Metal Cutting, Sales & Shipping | Buy Steel, Aluminum, Copper, Brass, Stainless | Metal Product Guides at OnlineMetals.com". www.onlinemetals.com. Retrieved 2016-06-16.
- ^ a b Central Steel & Wire Company Catalog (2006–2008 ed.), p. 246. Note: "For bar products; plate, sheet and tubing may be slightly different."
- ^ a b c d Central Steel & Wire Company Catalog (2006–2008 ed.), p. 260.
- ^ "4140 Steel". steel-bar.com.